Influence of photodynamic therapy, different final irrigants, and ultrasonic activation on the bond strength of glass fiber posts to root dentin.

OBJECTIVE: To evaluate the influence of photodynamic therapy (PDT), different final irrigants, and ultrasonic activation (US) on the bond strength of glass fiber posts (GFP) to root dentin. METHODS: One hundred twenty bovine roots were divided into 12 groups according to PDT application, the type of final endodontic irrigant, and US. The samples were divided into 12 groups (n = 10): G1-DW(distilled water); G2-DW+US; G3-17% EDTA; G4-17% EDTA+US; G5-17% GA (glycolic acid); G6-17% GA+US; G7-PDT+DW; G8-PDT+DW+US; G9-PDT+17% EDTA; G10-PDT+17% EDTA+US; G11-PDT+17% GA; G12-PDT+17% GA+US. After cementing the glass fiber posts with resin cement, roots were sectioned into 2-mm-thick slices. One slice from the cervical third and another from the middle third were used for the push out test (PO), and the other two for the diametral compression test (DC). Thus, 10 samples were obtained per third for each mechanical test (n = 10). Kruskal-Wallis and Student-Newman-Keuls tests were used to analyze PO and DC data, and Pearson's correlation test was used to verify the relationship between the variables. Failure patterns were analyzed with chi-square test. RESULTS: Significant differences were found in the PO test among the experimental groups (p < 0.001; power=1.00). PDT improved bond strength when using EDTA. PDT and US increased bond strength when using GA. Favorable failure patterns occurred more frequently in Group GA+US. There was no correlation between data obtained with PO and DC tests (r = 0.112; p = 0.729). CONCLUSION: PDT provided the highest bond strength values of GFP to root dentin when associated with GA and US or when associated only with EDTA.

Influence of ceramic primers on microshear bond strength to zirconia

This study aimed to investigate the effect of two ceramic primers on the microshear bond strength (µSBS) of yttria-stabilized zirconia (Y-TZP) to two types of self-adhesive resin cement and one BisGMA-based resin cement. Zirconia specimens were sandblasted with 27-µm aluminum oxide and composite cylinders were cemented with resin cement with or without the prior use of ceramic primers. Nine groups (n=12) were randomly distributed according to the cement (self-adhesive RelyX U200/3M ESPE, self-adhesive Maxcem Elite/Kerr, and BisGMA-based dual-cure RelyX ARC/3M ESPE) and ceramic primer (Z-Primer Plus/Bisco and Porcelain Liner M/Sun Medical Co.). After luting, the specimens were stored in distilled water at 37°C for 24 hours and then submitted to the µSBS test. The data were analyzed with two-way ANOVA followed by the Scheffe post hoc test (p<0.05). There were significant differences between RelyX U200 and other groups. There were also significant differences between the RelyX U200 group without ceramic primer and other groups without ceramic primers (p<0.05). Self-adhesive resin cement (RelyX U200 and MaxCem) presented higher microshear bond strength (6.17 and 2.32 MPa) than the conventional resin cement (RelyX ARC) when a porcelain primer was not used (0.43 MPa). When using Porcelain Liner M, the results of RelyX ARC (2.94 MPa) were equivalent to the results of self-adhesive cement (3.93 and 2.11 MPa). When using Z-Prime Plus, the results of MaxCem (5.36 MPa) were lower than those of RelyX U200 (9.59 MPa) but equivalent to those of RelyX ARC (6.07 MPa). When using the RelyX ARC, the use of both ceramic primers improved bond strength to zirconia. When using self-adhesive resin cement, Z-Prime Plus improved microshear bond strength values. It can be concluded that, after 24 hours, the highest µSBS results were obtained when using Z-Prime Plus and RelyX U200 self-adhesive cement.

Effect of glycolic acid and EDTA on dentin mechanical properties.

The aim of this study was to evaluate the effect of glycolic acid (GA) and EDTA on dentin mechanical properties. For the cohesive strength, flexural strength and fracture strength tests, the hourglass of root dentin, dentin sticks and roots standardised to 1 mm thickness were used respectively. ANOVA and Tukey tests were used for statistical analysis (P < 0.05). The results showed that EDTA and GA 17% reduced the cohesive strength values when compared to distilled water (control; P = 0.0022 and P = 0.0016 respectively), whereas the values for GA 10% group were similar to those of the control group (P = 0.093). No statistically significant difference was found among the groups for the flexural strength test (P = 0.1974). Fracture strength test showed that EDTA and GA 17% were statistically similar to each other (P = 0.7694) and statistically inferior to GA 10% (P = 0.0007 and P = 0.0004 respectively). It was concluded that 10% GA showed fewer negative effects on dentin mechanical properties.

Influence of the apical limit of instrumentation and photodynamic therapy on the postoperative pain of lower molars with asymptomatic apical periodontitis.

INTRODUCTION: The aim of present study was to evaluate the influence of apical limit of instrumentation and PDT on the postoperative pain of lower molars with asymptomatic apical periodontitis. METHODS: Forty patients were included in the present study and were divided into 4 groups (n=10), according to apical limit of instrumentation and use of PDT: instrumentation at 0.0 measurement; instrumentation at 0.0 measurement+PDT; instrumentation 1mm beyond 0.0 measurement; instrumentation 1mm beyond 0.0 measurement+PDT. In the PDT, the root canals were filled with 0.01% methylene blue, remaining for 5 min. The low-intensity laser was used with 100 mW, 660-690 nm wavelength), using intra-canal fibre. Root canals were irradiated for 90 s, delivering total dose of 9 J and energy density of 320 J/cm2. After root canal preparation and PDT protocols, root canals were filled with gutta-percha and AH Plus endodontic sealer, being sealed with composite resin.The evaluation of postoperative pain was performed by visual analog scale after 24, 48, 72 hours and 7 days. Data were analysed by specific statistical tests, at level of 5%. RESULTS: No statistical significant difference was observed among experimental groups in all evaluation periods, as well as in the intragroup analysis over time, regarding postoperative pain and analgesic medication consumption (p>0.05). CONCLUSIONS: Apical limit of instrumentation and PDT have no influence on the postoperative pain of lower molars with asymptomatic apical periodontitis.

Influence of glass fiber posts and class III direct restorations on the resistance of anterior teeth / Influência dos pinos de fibra de vidro e restaurações diretas classe III na resistência dos dentes anteriores

This study objectives to evaluate the fracture strength of upper central incisors (UCI) restored with composite resin (CR) in Class III cavities and endodontically treated teeth with or without glass fiber post (GFP), analyzing their failure mode. Sixty human UCI were randomly divided into four experimental groups: endodontically treated teeth without GFP (G1), endodontically treated teeth with GFP (G2), teeth with mesial/distal Class III cavities restored with CR without GFP (G3), and teeth with mesial/distal Class III cavities restored with CR with GFP (G4). The samples were submitted to the fracture strength test in a universal testing machine with a compression shear load applied at speed of 1.0 mm/min until fracture occurred. The data were submitted to one-way ANOVA (α=0.05) and the samples were analyzed for failure mode. The analysis did not show a significant statistical difference in fracture strength between the groups (p>0.05). The results showed that only endodontically treated teeth (G1) (753.4N) presented behavior similar to teeth with GFP (G2) (702.1N). The same occurred when comparing teeth with Class III cavities without GFP (G3) (670.2 N) and with GFP (G4) (746.1N). It can be concluded that glass fiber posts do not change the fracture strength of incisors with endodontic treatment and Class III cavities.

Este estudo objetiva avaliar a resistência à fratura de incisivos centrais superiores (ICS) restaurados com resina composta (RC) em cavidades Classe III e dentes tratados endodonticamente com ou sem pino de fibra de vidro (PFV), analisando seu padrão de fratura. Sessenta ICS humanos foram divididos aleatoriamente em quatro grupos experimentais: dentes tratados endodonticamente sem PFV (G1), dentes tratados endodonticamente com PFV (G2), dentes com cavidades mesiais/distais Classe III restauradas com RC sem PFV (G3), e dentes com cavidades mesiais/distais Classe III restauradas com RC com PFV (G4). As amostras foram submetidas ao teste de resistência à fratura em uma máquina universal de ensaios com uma carga de cisalhamento de compressão aplicada na velocidade de 1,0 mm / min até a ocorrência da fratura. Os dados foram submetidos à ANOVA unidirecional (α=0,05) e as amostras foram analisadas quanto ao modo de falha. A análise não mostrou diferença estatisticamente significativa na resistência à fratura entre os grupos (p>0,05). Os resultados mostraram que os dentes apenas tratados endodonticamente (G1) (753,4N) apresentaram comportamento semelhante aos dentes com PFV (G2) (702,1N). O mesmo ocorreu ao comparar dentes com cavidades Classe III sem PFV (G3) (670.2 N) e com PFV (G4) (746.1N). Pode-se concluir que pinos de fibra de vidro não alteram a resistência à fratura de incisivos com tratamento endodôntico e cavidades Classe III.

Removal of water binding proteins from dentin increases the adhesion strength of low-hydrophilicity dental resins.

OBJECTIVES: To investigate the role of proteoglycans (PGs) on the physical properties of the dentin matrix and the bond strength of methacrylate resins with varying hydrophilicities. METHODS: Dentin were obtained from crowns of human molars. Enzymatic removal of PGs followed a standard protocol using 1 mg/mL trypsin (Try) for 24 h. Controls were incubated in ammonium bicarbonate buffer. Removal of PGs was assessed by visualization of glycosaminoglycan chains (GAGs) in dentin under transmission electron microscopy (TEM). The dentin matrix swelling ratio was estimated using fully demineralized dentin. Dentin wettability was assessed on wet, dry and re-wetted dentin surfaces through water contact angle measurements. Microtensile bond strength test (TBS) was performed with experimental adhesives containing 6% HEMA (H6) and 18% HEMA (H18) and a commercial dental adhesive. Data were statistically analyzed using ANOVA and post-hoc tests (α = 0.05). RESULTS: The enzymatic removal of PGs was confirmed by the absence and fragmentation of GAGs. There was statistically significant difference between the swelling ratio of Try-treated and control dentin (p < 0.001). Significantly lower contact angle was found for Try-treated on wet and dry dentin (p < 0.002). The contact angle on re-wet dentin was not recovered in Try-treated group (p = 0.9). Removal of PGs significantly improved the TBS of H6 (109% higher, p < 0.001) and H18 (29% higher, p = 0.002) when compared to control. The TBS of commercial adhesive was not affected by trypsin treatment (p = 0.9). SIGNIFICANCE: Changing the surface energy of dentin by PGs removal improved resin adhesion, likely due to more efficient water displacement, aiding to improved resin infiltration and polymerization.

Effect of a new irrigant solution containing glycolic acid on smear layer removal and chemical/mechanical properties of dentin.

The objective of this study was to evaluate the effects of glycolic acid (GA) (with pH 1.2 and 5) and ethylenediaminetetraacetic acid (EDTA) on the chemical and mechanical properties of dentin to investigate the potential use of GA as final irrigant in the root canal therapy. Specifically, changes in microhardness, smear layer removal, erosion, mineral content distribution, apatite/collagen ratio and flexural strength of mineralized dentin treated with GA were assessed. Saline solution was used as a negative control. Knoop microhardness (KHN) was measured on the root canal lumen of root segments. Dentin beams were used for 3-point flexural strength (σ) test. Scanning electron microscopy (SEM) images of root sections were obtained for evaluation of smear layer removal and dentin erosion on root segments and energy dispersive X-ray spectroscopy (EDS) was used for mineral content distribution. The apatite/collagen ratio (A/C) in dentin powder were examined by Fourier transform infrared (FTIR) spectroscopy. KHN, σ and A/C results were statistically analyzed with ANOVA and Tukey tests (α = 0.05). Smear layer and dentin erosion scores were analyzed with Kruskal-Wallis and Dunn tests (α = 0.05). Root dentin treated with EDTA and GA presented similar KHN regardless of the pH (p > 0.05). However, KHN was significantly reduced in EDTA and GA groups when compared to control group (p<0.001). GA showed the same ability to remove the smear layer and to cause dentin erosion as EDTA. EDS results showed that the GA and EDTA solutions did not alter the dentin mineral content distribution. The apatite/collagen ratio reduced with all irrigant solution and was the lowest with GA pH 5 (p<0.001), while σ was not significantly affected by the experimental solutions (p = 0.559). It can be concluded that GA has similar ability to remove the smear layer than EDTA. GA does not affect negatively the chemical/mechanical properties and it does not increase dentin erosion. The use of GA with low pH seems to promote less change in collagen/apatite ratio, but further studies are needed to establish an ideal clinical protocol. Therefore, this study supports the potential use of GA as an alternative final irrigation solution for root canal preparation.

Antibacterial Efficacy of the Grape Seed Extract as an Irrigant for Root Canal Preparation.

Objective: The purpose of this research was to compare relative effectiveness of sodium hypochlorite 5.25% (NaOCl), 2% chlorhexidine gel (CHX) and 6.5 % grape seed extract (GSE) against Enterococcus faecalis using instrument Reciproc R25 in root canal preparation. Methods: Forty-five mesiobuccal root canals from extracted human maxillary molars were collected and infected with Enterococcus faecalis. The samples were divided into five groups according to the different types of irrigants: saline (positive control) (n=5); in the other groups were used 10 root canals for each group: NaOCl+EDTA; CHX gel+EDTA; GSE solution+EDTA; GSE gel+EDTA. All the groups were prepared with reciprocating instruments Reciproc R25. Bacterial reduction was measured by two-way ANOVA (P<0.001) followed by Tukey HSD post-hoc tests, from the counting of colony forming units (CFUs) from samples collected before instrumentation and after. The significance level established at 5% (P<0.05). Results: The group prepared with the NaOCl resulted in highest antimicrobial capacity among of all (P>0.05), followed by CHX and GSE gel (P<0.05). Control and GSE solution showed similar results (P<0.05) and resulted in the lowest percentage of the reduction of the microorganism into the root canals. Conclusion: NaOCl had the higher elimination capacity of Enterococcus faecalis than GSE and CHX.

Antimicrobial activity of intracanal dressings composed by natural products associated to chlorhexidine and its influence on dentinal colour change / Avaliação da ação antimicrobiana de medicações intracanais à base de produtos fitoterápicos associados à clorexidina e sua influência na alteração de cor da estrutura dentinária

Purpose: evaluate the antimicrobial activity of intracanal dressings and their influence on dentinal colour changes. Material and methods: eighty single-rooted human extracted teeth were decoronated and divided into eight groups (n=10) according to intracanal dressing protocols inserted into the root canals: G1­distilled water (DW); G2­2% chlorhexidine gel (CHX); G3­calcium hydroxide (Ca[OH]2)+DW; G4­grape seed extract (GSE)+DW; G5­ginger extract (GE)+DW; G6­Ca(OH)2+CHX; G7­GSE+CHX; and G8­GE+CHX. The antimicrobial activity was evaluated by colony-forming units (CFUs) counting and dentinal colour changes was evaluated by digital spectrophotometry. Data were statistically analysed by One-way ANOVA followed by Tukey´s post hoc test (antimicrobial evaluation) and non-parametric Wilcoxon followed by the Mann- Whitney-U test (colour change evaluation) (α=0.05). Results: the highest bacterial reduction was observed in groups 4, 6, 7 and 8, with no significant difference between them (p<0.05). Groups 4 and 7 showed the highest medians of dentinal colour change (p<0.05). Conclusion: the addition of CHX improved the antimicrobial activity of GE-based intracanal dressing, with no effect in GSE-based intracanal dressing; moreover, these protocols induced significant dentinal colour changes. (AU)

Objetivo: avaliar a atividade antimicrobiana de medicações intracanais e sua influência na alteração da cor dentinária. Materiais e métodos: oitenta dentes humanos extraídos unirradiculares foram seccionados e divididos em oito grupos (n = 10), de acordo com os protocolos de medicação intracanal inseridos nos canais radiculares: água destilada G1 (DW); G2-2% de gel de clorexidina (CHX); hidróxido de cálcio G3 ­ (Ca [OH] 2) + DW; extrato de semente de uva G4 (GSE) + DW; extrato de gengibre G5 (GE) + DW; G6- Ca (OH) 2 + CHX; G7 ­ GSE + CHX; e G8-GE + CHX. A atividade antimicrobiana foi avaliada por contagem de unidades formadoras de colônias (UFCs) e as alterações de cor dentinária foram avaliadas por espectrofotometria digital. Os dados foram analisados estatisticamente por ANOVA one-way, seguida pelo teste post hoc de Tukey (avaliação antimicrobiana) e Wilcoxon não paramétrico, seguido pelo teste de Mann- Whitney-U (avaliação da mudança de cor) (α = 0,05). Resultados: a maior redução bacteriana foi observada nos grupos 4, 6, 7 e 8, sem diferença significativa entre eles (p < 0,05). Os grupos 4 e 7 apresentaram as maiores medianas da alteração da cor dentinária (p < 0,05). Conclusão: a adição de CHX melhorou a atividade antimicrobiana da medicação intracanal baseado em GE, sem efeito na medicação intracanal baseado em GSE; além disso, esses protocolos induziram alterações significativas na cor dentinária.(AU)

Glycolic acid: Characterization of a new final irrigant and effects on flexural strength and structural integrity of dentin.

The aim of this study was to characterize glycolic acid (GA) and examine its effects on powder and flexural strength of dentin. Particle size and energy-dispersive EDS in GA powder was performed for chemical analysis. Surface tension and pH levels of ethylenediaminetetraacetic acid (EDTA), citric acid (CA), and GA solutions were evaluated at different times and temperatures. Dentin powder and mineralized dentin beams were immersed for 1 min in EDTA, CA, or GA solutions and subjected to Fourier transform infrared spectroscopy for apatite/collagen ratio analysis and 3-point flexure test, respectively. GA showed the largest particle size (µm), and its surface tension was similar to that of EDTA and CA. Surface tension decreased in solutions of higher concentrations. GA showed pH stability at all times and temperatures evaluated. The apatite/collagen ratio reduced with increased GA concentrations, while flexural strength was not significantly affected by GA concentration. GA seems a good choice as a final irrigation solution after root canal preparation.

Antimicrobial activity of glycolic acid as a final irrigant solution for root canal preparation.

The objective of this study was to evaluate the antimicrobial capacity of glycolic acid (GA) at different concentrations as a final irrigant during the preparation of root canals. The sample consisted of 77 extracted single-rooted human teeth with complete root formation, no previous endodontic treatment, and a root length of at least 14 mm. The root canals were prepared in a standardized manner with a rotary file system. During this process, irrigation was performed with 2.5% sodium hypochlorite (NaOCl), and the final irrigant was 17% ethylenediaminetetraacetic acid (EDTA). After the root canal sterilization procedure, Enterococcus faecalis was cultured in a Petri dish, and 70 sterilized root canals were inoculated with a suspension containing 3.0 × 108 colony-forming units (CFUs) per milliliter. The roots were divided into 7 groups (n = 10) according to the following solutions: 0.9% sodium chloride (NaCl); 6% NaOCl; 17% EDTA; 10%, 17%, or 25% GA; or 17% citric acid (CA). The capacity of the different substances to reduce E faecalis was evaluated by counting the CFUs before and after treatment with the final irrigant solutions. Data were subjected to an analysis of variance and the Tukey test at a 5% significance level. The greatest bacterial reduction was observed in the group irrigated with NaOCl (P < 0.05). There were no statistically significant differences among the groups irrigated with GA in different concentrations (P > 0.05), but they all demonstrated greater disinfection capacity than CA and EDTA (P < 0.05). CA showed significantly greater antimicrobial capacity than EDTA (P < 0.05). EDTA showed significantly greater antimicrobial capacity only in relation to NaCl (P < 0.05). At different concentrations, GA demonstrated greater capacity to eliminate E faecalis from root canals than did EDTA.

Association of calcium hypochlorite, reciprocating instrumentation and photodynamic therapy: Antimicrobial analysis and effects on root dentin structure.

INTRODUCTION: This study aimed to evaluate the antimicrobial action of calcium hypochlorite(Ca[OCl]2) and sodium hypochlorite (NaOCl) with reciprocating instrumentation and photodynamic therapy(PDT), and its influence on root dentin structure. METHODS: One hundred and ten human teeth were used to antimicrobial evaluation, inoculated with Enterococcus faecalis and divided into 11 groups (n = 10): G1 - distilled water(control); G2-1 % NaOCl; G3-5.25 % NaOCl; G4-1 % Ca(OCl)2; G5-5.25 % Ca(OCl)2; G6-PDT; G7-distilled water + PDT; G8-1 % NaOCl + PDT; G9-5.25 % NaOCl + PDT; G10-1 % Ca(OCl)2+PDT; G11-5.25 % Ca(OCl)2+PDT. In all groups, except G6, the root canals were instrumented with #R50 Reciproc file in the working length in association with tested chemical auxiliary substance. The counting of colony forming units (CFUs) was performed to calculate the bacterial percentage reduction of each group. Following, 55 bovine teeth were used to microhardness evaluation and divided into the same 11 groups (n = 5), with no instrumentation and immersion in the tested protocols. The modification of root dentin microhardness was evaluated by using the Vicker tester. Finally, 33 bovine teeth were used to organic components evaluation and divided into the same 11 groups (n = 3), with no instrumentation and immersion in the tested protocols. The modification of organic components of root dentin was evaluated by light microscopy. Specific statistical analysis was performed for each evaluation. RESULTS: The higher bacterial reduction was observed in groups 3,4,5,8,9,10 and 11, with no statistical difference between them (p > 0.05). The higher microhardness reduction was observed in groups 8,9,10 e 11, with no statistical difference between them (p > 0.05). The highest modification on organic components was observed in groups 3,5,9 and 11, with no statistical difference between them (p > 0.05). CONCLUSIONS: The association of Ca(OCl)2, reciprocating instrumentation and PDT promotes effective antimicrobial action. Moreover, lower modification was induced in microhardness and organic components of root dentin, by using Ca(OCl)2 in low concentration associated to PDT.

Glycolic acid as the final irrigant in endodontics: Mechanical and cytotoxic effects.

The aim of this study was to investigate the effects of glycolic acid (GA) on the microhardness, roughness, dentin mineral content distribution; smear layer removal and cytotoxicity. One hundred human teeth were randomly divided into six groups: distilled water (control group), 17% EDTA, 10% citric acid (CA), 5% GA, 10% GA, and, 17% GA. Microhardness and roughness were measured in the canal lumen. Scanning electron microscopy (SEM) images (2000×) for smear layer removal evaluation; energy dispersive X-ray spectroscopy (EDS) for chemical analysis. Cell viability assay was made on fibroblast cells. The lowest microhardness and higher roughness were observed for 17% GA. GA showed the ability to remove the smear layer to a similar level as EDTA and CA, with no statistical difference between the concentrations used. GA and CA were cytotoxic in a dose-dependent manner. GA showed potential as an endodontic agent for final irrigation in root canal terapies.

Structural and biomechanical changes to dentin extracellular matrix following chemical removal of proteoglycans.

Proteoglycans are biomacromolecules with significant biomineralization and structural roles in the dentin extracellular matrix. This study comprehensively assessed the mechanical properties and morphology of the dentin extracellular matrix following chemical removal of proteoglycans to elucidate the structural roles of proteoglycans in dentin. Dentin extracellular matrix was prepared from extracted teeth after complete tissue demineralization. Chemical removal of proteoglycans was carried-out using guanidine hydrochloride for up to 10 days. The removal of proteoglycans was determined by dimethylmethylene blue colorimetric assay and histological staining analyses using transmission electron microscopy and optical microscopy. The modulus of elasticity of dentin matrix was determined by a 3-point bending test method. Partial removal of proteoglycans induced significant modifications to the dentin matrix, particularly to type I collagen. Removal of proteoglycans significantly decreased the modulus of elasticity of dentin extracellular matrix (p < 0.0001). In conclusion, the subtle disruption of proteoglycans induces pronounced changes to the collagen network packing and the bulk modulus of elasticity of dentin matrix.

Fracture Strength and Stress Distribution in Premolars Restored with Cast Post-and-Cores or Glass-Fiber Posts Considering the Influence of Ferule.

OBJECTIVES: The aim of this study was to evaluate the influence of ferule and the post type on the fracture strength and stress distribution in premolars. MATERIALS AND METHODS: Forty human mandibular premolars were decoronated, allocated in four groups, and restored as follows: CPC-NF: cast post-and-core and absence of ferule; CPC-F: cast post-and-core and presence of ferule; FPC-NF: glass-fiber posts and absence of ferule; FPC-F: glass-fiber posts and presence of ferule. The fracture strength (FS) and failure patterns were evaluated. Finite element analysis (FEA) evaluated the stress distribution. RESULTS: FS did not differ between CPCs and FPC either in presence or in absence of ferule. The presence of ferule increased FS with both post types. Mean values of FS for ferule groups were higher than functional or parafunctional loads reported in literature, which was not the case for FPC-NF when compared to parafunctional loads. FEA with a functional load showed slightly higher compressive stresses in dentin in the group CPC-NF, which was much lower than the compressive strength of dentin. Lower percentage of catastrophic failures was observed in nonferule groups irrespective of post type, which was explained by the stress concentration in the cervical root region when FEA with the FS load was simulated. CONCLUSION: Ferule effect was shown to be more important than post type in the analysis. Both posts showed potential to withstand functional loads irrespective of presence of ferule. However, the mean FS was lower than parafunctional loads for FPC in the absence of ferule.

Antibacterial Efficacy of Synthetic and Natural-Derived Novel Endodontic Irrigant Solutions.

The aim of this study was to compare the efficacy of grape seed extract (GSE), calcium hypochlorite [Ca(ClO)2], and sodium hypochlorite (NaOCl) irrigant solutions with rotary or reciprocating instrumentation for disinfection of root canals inoculated with Enterococcus faecalis. The mesiobuccal root canals of mandibular molars were prepared and inoculated with Enterococcus faecalis for 21 days. The roots were then randomly divided into the following eight experimental groups (n=11) according to the instrumentation technique and disinfection protocol: ProTaper Next or Reciproc R25 with sodium chloride (control group), 6% NaOCl, 6% Ca(ClO)2, or 50% GSE used for irrigation during instrumentation. The antimicrobial activity was determined on the basis of a reduction in colony-forming units (CFUs) counted on bacterial samples collected before and after root canal instrumentation and expressed as a percentage of reduction. Data were evaluated by two-way ANOVA followed by Tukey HSD post-hoc tests (p<0.05). No significant differences were observed in bacterial reduction between the ProTaper Next and Reciproc R25 systems (p>0.05), regardless of the irrigant solution used. Furthermore, all active solutions (6% NaOCl, 50% GSE, and 6% Ca(ClO)2) showed similar potential to reduce bacterial counts (p>0.05) and were significantly more effective than sodium chloride (control) (p<0.05). The results suggest that the GSE and Ca(ClO)2 have potential clinical application as irrigant solutions in endodontic therapy since they present bactericidal efficacy against Enterococcus faecalis.

Efficacy of Natural Collagen Crosslinkers on the Compromised Adhesive Bond Strength to NaOCl-treated Pulp Chamber Dentin.

PURPOSE: To evaluate the efficacy of natural collagen crosslinkers on compromised adhesive bond strength to NaOCl-treated pulp chamber dentin. MATERIALS AND METHODS: Mesial surfaces of the pulp chamber dentin of 120 extracted human molars were obtained. The dentin fragments were divided into six groups according to the protocols used: no treatment (negative control), sodium hypochlorite (NaOCl) for 30 min and final irrigation with 17% EDTA for 3 min (positive control). After treatment with NaOCl and EDTA, the dentin surfaces of the experimental groups were treated for 5 min with one of the following: grape seed extract (GSE), tannic acid (TA), green tea (GT), or n-acetyl cysteine (NAC). Half of the samples of each group were bonded with an etch-and-rinse (Single Bond; 3M Oral Care) and the other half using a self-etch (Scotchbond Universal; 3M Oral Care) adhesive. The restoration was completed with composite. The bonded specimens were sectioned to produce sticks and subjected to the microtensile bond strength test. Data were analyzed by two-way ANOVA and Tukey's HSD test (p < 0.05). RESULTS: Both adhesives had similar bond strengths (p > 0.05). The NaOCl-treated group had significantly lower bond strength than the negative control (p < 0.05). The application of NAC did not recover compromised bonding (p > 0.05). On the other hand, GSE, TA and GT had significant reversal effects of the bond strengths to NaOCl-treated dentin (p < 0.05). CONCLUSION: Compromised bonding of adhesives to NaOCl-treated dentin can be reversed by the application of either GSE, TA or GT.

Antibacterial efficacy of synthetic and natural-derived novel endodontic irrigant solutions

Abstract The aim of this study was to compare the efficacy of grape seed extract (GSE), calcium hypochlorite [Ca(ClO)2], and sodium hypochlorite (NaOCl) irrigant solutions with rotary or reciprocating instrumentation for disinfection of root canals inoculated with Enterococcus faecalis. The mesiobuccal root canals of mandibular molars were prepared and inoculated with Enterococcus faecalis for 21 days. The roots were then randomly divided into the following eight experimental groups (n=11) according to the instrumentation technique and disinfection protocol: ProTaper Next or Reciproc R25 with sodium chloride (control group), 6% NaOCl, 6% Ca(ClO)2, or 50% GSE used for irrigation during instrumentation. The antimicrobial activity was determined on the basis of a reduction in colony-forming units (CFUs) counted on bacterial samples collected before and after root canal instrumentation and expressed as a percentage of reduction. Data were evaluated by two-way ANOVA followed by Tukey HSD post-hoc tests (p<0.05). No significant differences were observed in bacterial reduction between the ProTaper Next and Reciproc R25 systems (p>0.05), regardless of the irrigant solution used. Furthermore, all active solutions (6% NaOCl, 50% GSE, and 6% Ca(ClO)2) showed similar potential to reduce bacterial counts (p>0.05) and were significantly more effective than sodium chloride (control) (p<0.05). The results suggest that the GSE and Ca(ClO)2 have potential clinical application as irrigant solutions in endodontic therapy since they present bactericidal efficacy against Enterococcus faecalis.

Resumo O objetivo deste estudo foi comparar a eficácia do extrato de semente de uva (ESU), hipoclorito de cálcio [Ca(ClO)2] e hipoclorito de sódio (NaOCl) como soluções irrigadores quando utilizadas com instrumentos reciprocantes e rotatórios para desinfecção de canais radiculares infectados com Enterococcus faecalis. Raízes mesio-vestibulares de molares inferiores foram preparados e inoculados com E. faecalis por 21 dias. As raízes foram aleatoriamente divididas em 8 grupos (n=11) de acordo com a técnica de instrumentação e protocolo de irrigação: ProTaper Next ou Reciproc R25 associados com soro fisiológico (grupo controle), Ca(ClO)2 6%, NaOCl 6% ou ESU 50%. A atividade antimicrobiana foi determinada pela redução do número de Unidades Formadoras de Colonias (UFCs) coletadas antes e após a instrumentação e expressas em porcentagens de redução. Os dados foram analisados estatisticamente pelos testes ANOVA seguido pelo teste complementar de Tukey HSD (p<0,05). Não foi encontrado diferença estatisticamente significante na redução bacteriana entre os sistemas ProTaper Next e Reciproc R25 (p>0.05), independente da solução irrigadora usada. Além disso, todas as soluções ativas (NaOCl, ESU e Ca(ClO)2) mostraram similar potencial em reduzir a quantidade de bactérias (p>0.05) e foram significativamente mais efetivas que o soro fisiológico (p<0.05). Pode-se concluir que o ESU e o Ca(ClO)2 apresentam potencial para aplicação clínica como irrigantes endodônticos uma vez que apresentaram efetividade antimicrobiana contra o E. faecalis.

Does adding an instrument after root preparation with Reciproc® R25 increase bacterial reduction?

AIM: The aim of this study was to compare the bacterial reduction achieved with reciprocating instruments such as Reciproc® R25 (VDW GMBH, Munich, Germany) and Reciproc® R25 combined with rotary file Mtwo 40.04 (VDW GMBH) during root canal preparation. MATERIALS AND METHODS: Fifty mesiobuccal root canals of maxillary molars were contaminated with Enterococcus faecalis broth culture and then an initial bacterial sample was collected from the root canal with paper cones and plated on brain-heart infusion agar. The root canals were divided into four groups as follows: Reciproc® R25 (n = 20) and Reciproc® R25 combined with Mtwo 40.04 instrument (n = 20). The negative controls consisted of five uncontaminated root canals and the positive control consisted of five contaminated roots that were not subjected to any decontamination procedure. Irrigation was performed using sodium chloride. After instrumentation, samples were collected with paper cones and the rate of bacterial reduction was calculated. Microbiological testing (colony-forming units [CFUs]) was performed to quantify the decontamination obtained by the proposed protocols. Statistical analysis was performed by paired t-test and analysis of variance test. RESULTS: Both techniques significantly reduced the number of bacteria in the root canal (P < 0.05), with no significant difference among them (P > 0.05). CONCLUSION: The addition of the instrument Mtwo 40.04 after the root preparation with the instrument R25 does not improve its decontamination capability.

Role of proteoglycans on the biochemical and biomechanical properties of dentin organic matrix.

OBJECTIVE: Proteoglycans (PGs) are multifunctional biomacromolecules of the extracellular matrix of collagen-based tissues. In teeth, besides a pivotal regulatory role on dentin biomineralization, PGs provide mechanical support to the mineralized tissue and compressive strength to the biosystem. This study assessed enzymatic protocols for selective PGs removal from demineralized dentin to determine the roles of these biomacromolecules in the bulk mechanical properties and biostability of type I collagen. METHODS: Selective removal of glycosaminoglycans chains (GAGs) and PGs from demineralized dentin was carried out by enzymatic digestion protocols using chondroitinase ABC (c-ABC) and trypsin (Try). A comprehensive study design included assessment of dentin matrix mass loss, biodegradability of the PGs/GAGs-depleted dentin matrix, ultimate tensile strength (UTS) and energy to fracture tests. Quantitative data was statistically analyzed by two-way and one-way ANOVA followed by the appropriate post hoc tests (α=0.05). RESULTS: Transmission electron microscopy images show effective GAGs removal by c-ABC and Try and both enzymatic methods released statistically similar amounts of GAGs from the demineralized dentin. Try digestion resulted in about 25% dentin matrix mass loss and increased susceptibility to collagenolytic digestion when compared to c-ABC (p=0.0224) and control (p=0.0901). Moreover, PGs digestion by Try decreased the tensile strengths of dentin. Statistically lower energy to fracture was observed in c-ABC-treated dentin matrix. CONCLUSIONS: GAGs plays a pivotal role on tissue mechanics and anisotropy, while the core protein of PGs have a protective role on matrix biostability.